阻燃级PA6T 日本三井化学 C430N 玻纤增强 低吸水 耐化学性电气应用
阻燃级PA6T 日本三井化学 CRLEN™ C430N
聚酰胺 6T
30% 玻璃纤维增强材料
Mitsui Chemicals, Inc.
产品说明:ARLEN™ C430N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ C430N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating.
Features:
High dimensional stability
High melting point
High rigidity
Minimum water absorption
Good chemical and heat resistance
Flame retardant
Applications:
Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.
C430N 物性表
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 比重 | 1.66 | g/cm3 | ASTM D792 |
| 收缩率 | ASTM D955 | ||
| 流动 | 0.30 | % | ASTM D955 |
| 横向流动 | 0.70 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr, 65%r.h) | 2.0 | % | ASTM D570 |
| 洛氏硬度 (M 级) | 95 | ASTM D785 |
| 抗张强度 | 170 | MPa | ASTM D638 |
| 伸长率 (断裂) | 3.0 | % | ASTM D638 |
| 弯曲模量 | 11400 | MPa | ASTM D790 |
| 弯曲强度 | 250 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | 85 | J/m | ASTM D256 |
| 载荷下热变形温度 (1.8 MPa, 未退火) | 295 | °C | ASTM D648 |
| 玻璃转化温度 | 85.0 | °C | |
| 熔融温度 | 310 | °C | |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 | 1.2E-5 | cm/cm/°C | ASTM E831 |
| 横向 | 9.2E-5 | cm/cm/°C | ASTM E831 |
| 体积电阻率 | 1.0E+15 | ohms·cm | ASTM D257 |
| 介电强度 | 26 | kV/mm | ASTM D149 |
| 介电常数 (1 MHz) | 4.00 | ASTM D150 | |
| 耗散因数 (1 MHz) | 0.013 | ASTM D150 |
| UL 阻燃等级 | V-0 | UL 94 |
30N 玻纤增强 低吸水 耐化学性电气应用